Bismuth niobate (BiNbO4) has attracted attention as a low-fired ceramics with promising microwave application potential. BiNbO4 ceramics was fabricated by mixed oxide method and sintered at temperature T<1000˚C. As the sintering aids a small amount of CuO oxide was used. The crystalline structure of the ceramic samples was examined by X-ray diffraction method at room temperature. The Rietveld refinement method was used for analysis of diffraction data. As a result an influence of dopants on crystal structure of bismuth niobate (BiNbO4) ceramics was revealed. It was found that fabricated BiNbO4 ceramics adopted the orthorhombic symmetry (αBiNbO4 phase, Pnna (52) space group). Small differences in elementary cell parameters were found.