Non-conducting BaO-B2O3-Al2O3-SiO2 parent glasses designed for solid oxide fuel cell (SOFC) sealing applications were prepared using the melt-quenching technique. The glass formation region was determined according to phase equilibrium relations and was found to be in the composition range 70BaO-(x)Al2O3-(10−x)B2O3-20SiO2 where 3.0 < x < 6.0 wt%. The conductivity values obtained conductivity ranged from 10−5 to 10−10 S/cm at temperatures between 600 and 850 °C. The batch compositions presented a threshold of dc conductivity near 70BaO wt% with a quasi linear behavior with the decrease of the BaO content. Different values of conduction activation energy were observed at temperatures above the glass transition temperature (Tg) (up to 700 °C), which were attributed to the thermal bond-breaking of non-bridging oxygen (NBO) defects. The experimental results of the electrochemical characterization by impedance spectroscopy of glass–ceramic interfaces with yttria-stabilized zirconia (YSZ) acting as solid ionic conductor electrolyte are presented and discussed.
Authors
- M Da,
- W Pontuschka,
- J Bartolomé,
- prof. dr hab. inż. Piotr Jasiński link open in new tab ,
- dr hab. inż. Jakub Karczewski link open in new tab ,
- Signo Reis
Additional information
- DOI
- Digital Object Identifier link open in new tab 10.1016/j.jeurceramsoc.2019.03.027
- Category
- Publikacja w czasopiśmie
- Type
- artykuł w czasopiśmie wyróżnionym w JCR
- Language
- angielski
- Publication year
- 2019