The aim of the presented study was to deposit protective-conducting Mn1.45Co1.45Fe0.1O4 and Mn1.5Co1.5O4 spinel coatings on the Crofer 22 H ferritic steel by means of electrophoresis and to evaluate their physicochemical properties after high-temperature oxidation under thermal cycling conditions. When the Crofer 22 H steel – whether uncoated or coated with the two spinels – was oxidized in 48-h cycles involving a temperature of either 750 or 800 °C, its oxidation kinetics approximately obeyed the parabolic rate law. The oxidation rate observed for uncoated steel was higher than that for the studied coating/steel systems. The Fe-doped spinel coating material improved the oxidation resistance of steel to a higher degree than the undoped spinel coating. The obtained bulk spinels exhibited a regular phase composition and high electrical conductivity, while the Mn1.45Co1.45Fe0.1O4 and Mn1.5Co1.5O4 coatings were dual-phase, compact, and exhibited good adhesion to the metallic substrate. The area-specific resistance values measured for the steel/coating systems indicate that the coatings significantly improve the electrical properties of the studied ferritic steel, especially at 800 °C. The conducted research confirmed the suitability of the Mn1.45Co1.45Fe0.1O4 and Mn1.5Co1.5O4 spinels as coatings on the Crofer 22 H ferritic steel to be applied in the production of interconnects used in intermediate-temperature SOFCs.
Authors
- M Bednarz,
- dr hab. inż. Sebastian Molin link open in new tab ,
- mgr inż. Michał Bobruk,
- M Stygar,
- E Długoń,
- M Sitarz,
- Tomasz Brylewski
Additional information
- DOI
- Digital Object Identifier link open in new tab 10.1016/j.matchemphys.2018.12.090
- Category
- Publikacja w czasopiśmie
- Type
- artykuł w czasopiśmie wyróżnionym w JCR
- Language
- angielski
- Publication year
- 2019