The design of efficient electrocatalysts for oxygen evolution reaction (OER) is an essential task in developing sustainable water splitting technology for the production of hydrogen. In this work, manganese cobalt spinel oxides with a general formula of MnxCo3-xO4 (x=0, 0.5, 1, 1.5, 2) were synthesised via a soft chemistry method. Non-equilibrium mixed powder compositions were produced, resulting in high electrocatalytic activity. The oxygen evolution reaction was evaluated in an alkaline medium (1 M KOH). It was shown that the addition of Mn (up to x ≤ 1) to the cubic Co3O4 phase results in an increase of the electrocatalytic performance. The lowest overpotential was obtained for the composition designated as MnCo2O4, which exhibited a dual-phase structure (~30% Co3O4 + 70% Mn1.4Co1.6O4): the benchmark current density of 10 mA cm-2 was achieved at the relatively low overpotential of 327 mV. The corresponding Tafel slope was determined to be ~79 mV dec-1. Stabilities of the electrodes were tested for 25 hours, showing degradation of the MnCo2O4 powder, but no degradation, or even a slight activation for other spinels.

Authors

• Krystian Lankauf link open in new tab ,
• dr inż. Karolina Cysewska link open in new tab ,
• dr hab. inż. Jakub Karczewski link open in new tab ,
• dr hab. inż. Aleksandra Mielewczyk-Gryń link open in new tab ,
• dr inż. Karolina Górnicka link open in new tab ,
• dr inż. Grzegorz Cempura,
• Ming Chen,
• prof. dr hab. inż. Piotr Jasiński link open in new tab ,
• dr hab. inż. Sebastian Molin link open in new tab