Ce0.8Gd0.2O1.9 (CGO) barrier layers are required to mitigate the chemical reactions between Sr-containing oxygen electrode materials and Zr-based oxygen ion conductors in high-temperature solid oxide cells. Barrier layers produced by different methods were studied in this work. As a reference, a cell with no barrier layer was measured. The application of the powder-processed barrier layers, considerably increases the performance. For further comparison, thin and dense CGO layers were produced by a low-temperature spray pyrolysis process. Three different thicknesses were evaluated: ∼300 nm, ∼700 nm and ∼1500 nm. The best performance was found for the ∼700 nm thick CGO barrier layer. It showed low ohmic and polarisation resistances. The low thickness and high density of the CGO barrier layer were found to be the important factors. The cells with the ∼700 nm CGO barrier layers were also evaluated for their electrolysis performance as well as fuel cell durability.
Authors
Additional information
- DOI
- Digital Object Identifier link open in new tab 10.1016/j.jeurceramsoc.2020.06.006
- Category
- Publikacja w czasopiśmie
- Type
- artykuły w czasopismach
- Language
- angielski
- Publication year
- 2020