The development of bacterial infection of the tissues surrounding an implant is one of the leading causes of implant surgery failure. In order to prevent the deposition of bacteria on the implant surface and the formation of biofilm, coatings that exhibit antibacterial properties are manufactured. However, the problem is the controlled release of the therapeutic substance from the coating over the extended life of the implant [1], [2]. Usually, the active substance is released immediately when the implant is inserted into an environment simulating human body fluids, which results in burst release phenomenon, namely, the release of a large dose of active substance in a short period of time, which may result in a toxic effect. Unfortunately, chitosan, one of the most commonly used biopolymers in controlled drug delivery systems, is unstable in neutral pH environments, readily absorbs water, and swells, resulting in rapid release of the therapeutic agent. Therefore, it is necessary to limit the dissolution rate of the chitosan coating at neutral pH. Previous studies [3] have confirmed that the addition of Eudragit E 100, a cationic copolymer based on dimethylaminoethyl methacrylate, butyl methacrylate, and methyl methacrylate in a 2:1:1 ratio, to chitosan coatings significantly reduced the degradation of these coatings in artificial saliva solution at neutral pH while maintaining high sensitivity to pH drop. Hence, a biopolymer matrix of this type should provide a good carrier for an active substance, such as metallic nanoparticles with antibacterial activity, which will be released only when inflammation of peri-implant tissues occurs. The scientific objective of this study was to fabricate a smart composite coating of chitosan/Eudragit E 100/silver nanoparticles (chit/EE100/AgNPs) on grade 2 titanium surface using variable deposition parameters such as AgNPs concentration, voltage, and deposition time by the electrophoretic method. The determinant of the process of creating such composite coatings with EE100 by electrophoretic method on the surface of Ti grade 2 has not been determined yet. No publication concerning investigations of coatings containing chitosan/EE100 with silver nanoparticles has been found. The microstructure, surface roughness, thickness, chemical and phase composition, mechanical and electrochemical properties, silver release rate at different pH, and wettability of the produced coatings were investigated...

Authors

• dr inż. Łukasz Pawłowski link open in new tab ,
• prof. dr hab. inż. Andrzej Zieliński link open in new tab