Results of the finite element analysis show that a far-side defect in a steel plate, with the depth greater by 10% of the plate thickness than a near-side defect, can produce a very similar magnetic flux leakage (MFL) signal. Due to the fact that a measurement of MFL itself can lead to misclassification of a far-side defect as a near-side one, and thus to underestimation of its depth, a comparative study of three complementary magnetic techniques was performed. The following techniques were studied: surface topology air-gap reluctance system (STARS), residual magnetic flux leakage (RMFL) and stray magnetic flux leakage (SMFL). Numerical results showed that in the case of the STARS and SMFL, defect signatures in signals were observed for investigated near-side defects, but not for far-side defects. The signature of the far-side defect in the RMFL was observed, however its peak-to-peak value was only about 8% of the value corresponding to the near-side defect.
Authors
Additional information
- DOI
- Digital Object Identifier link open in new tab 10.1007/s10921-022-00844-7
- Category
- Publikacja w czasopiśmie
- Type
- artykuły w czasopismach
- Language
- angielski
- Publication year
- 2022