In this study, intermediate-temperature solid oxide fuel cells (IT-SOFCs) with a nine-layer structure are constructed via a simple method based on the cost-effective tape casting-screen printing-co-firing process with the structure composed of a NiO-based four-layer anode, a Sm0.2Ce0·8O2-δ(SDC)/La0·8Sr0.2Ga0.8Mg0·2O3−δ (LSGM)/SDC tri-layer electrolyte, and an La0·6Sr0·4Co0·2Fe0·8O3-δ (LSCF)-based bi-layer cathode. The resultant SDC (4.14 μm)/LSGM (1.47 μm)/SDC (4.14 μm) tri-layer electrolyte exhibits good continuity and a highly dense structure. The Ro and Rp values of the single cell are observed to be 0.15 and 0.08 Ω cm2 at 800 °C, respectively, and the MPD of the cell is 1.08 Wcm-2. The high MPD of the cell appears to be associate with the significantly lower area-specific resistance and the reasonably high OCV. Compared to those with a similar electrolyte thickness reported in prior studies, the nine-layer anode-supported IT-SOFC with a tri-layer electrolyte developed by the study demonstrates superior cell properties.
Authors
- Sea-Fue Wang,
- Hsi-Chuan Lu,
- Yung-Fu Hsu,
- prof. dr hab. inż. Piotr Jasiński link open in new tab
Additional information
- DOI
- Digital Object Identifier link open in new tab 10.1016/j.ijhydene.2021.11.132
- Category
- Publikacja w czasopiśmie
- Type
- artykuły w czasopismach
- Language
- angielski
- Publication year
- 2022