This paper presents the results of calorimetric and strength tests of mortars with ordinary Portland cement and two substitution rates (10 and 20%) of cement by siliceous fly ash. The prepared samples were cured under isothermal conditions at four different temperatures: 23, 33, 43 and 53 °C. Heat of hydration was measured using an isothermal calorimeter dedicated to monitor the hydration process of cementitious composites such as paste, mortar and concrete. Thermal data were recorded continuously for 7 days, while compression tests were performed at 6 h and 1, 2, 5, 7 and 14 days of hardening. The studies proved that the amount of heat released correlates with the early-age strength of 50 mm mortar cubes. In the case of samples cured at 23 and 53 °C, a linear relationship between the heat of hydration and compressive strength was observed. The high value of the coefficient of determination (R2) allows one to estimate the mortar compressive strength after 7 and 14 days based on hydration heat tests conducted at standard temperature (23 °C), regardless of the percentage of siliceous fly ash. The increased curing temperatures do not guarantee a high correlation between compressive strength and the amount of heat released.
Authors
Additional information
- DOI
- Digital Object Identifier link open in new tab 10.3390/min12111471
- Category
- Publikacja w czasopiśmie
- Type
- artykuły w czasopismach
- Language
- angielski
- Publication year
- 2022