Rigid polyurethane foams (rPUs) were synthesized by replacing 35 and 70 wt.% of petrochemical polyol with polyglycerol. Two types of polyglycerol with different molecular weights and hydroxyl numbers were used to obtain new ‘‘green’’ polyurethane–polyglycerol foams. The foams were prepared by a single step method for the ratio of NCO/OH groups equal to 2. rPUs synthesized with polyglycerol showed regular cellular structure, with cell diameters comparable to those of reference foam. The apparent density and compressive strength of foams increased with increasing content of polyglycerols. The highest compressive strength of 240 kPa was observed for the foam containing 70 wt.% of polyglycerol PGK. In the case of foams comprising 35 wt.% of polyglycerols and the reference foam synthesized with petrochemical polyol only, the values of thermal stability, thermal conductivity (k value) and closed cell content were comparable.
Autorzy
- dr hab. inż. Łukasz Piszczyk link otwiera się w nowej karcie ,
- dr hab. inż. Michał Strankowski link otwiera się w nowej karcie ,
- mgr inż. Magdalena Danowska link otwiera się w nowej karcie ,
- dr inż. Aleksander Hejna link otwiera się w nowej karcie ,
- prof. dr hab. inż. Józef Haponiuk link otwiera się w nowej karcie
Informacje dodatkowe
- DOI
- Cyfrowy identyfikator dokumentu elektronicznego link otwiera się w nowej karcie 10.1016/j.eurpolymj.2014.05.012
- Kategoria
- Publikacja w czasopiśmie
- Typ
- artykuł w czasopiśmie wyróżnionym w JCR
- Język
- angielski
- Rok wydania
- 2014
Źródło danych: MOSTWiedzy.pl - publikacja "Rigid polyurethane foams from a polyglycerol-based polyol" link otwiera się w nowej karcie