The Ge0.77Ag0.1Sb0.13Te1alloy was fabricated by a novel two step route. For that purpose firstly the oxide reagents were melted at high temperature and quenched into pellets. After that pellets were milled to the powder and then reduced in hydrogen at various temperatures and for various periods of time. Energy dispersive X-ray analysis indicated the possibility of successful fabrication of stoichiometric thermoelectric materials from Te-Ag-Ge-Sb (TAGS) group. The electrical conductivity and Seebeck coefficient have been determined over temperature range from +20 °C up to +340 °C in argon atmosphere. It was also shown that for most of the fabricated samples the size of crystallites as well as electrical parameters like electrical conductivity, Seebeck coefficient and figure of merit (ZT) increases with the increasing time of reduction.The highest value of ZT (~1.0 at 340oC) was obtained for samples reduced in hydrogen atmosphere at 400oC for 20h and 40h.

Autorzy

• prof. dr hab. inż. Bogusław Kusz link otwiera się w nowej karcie ,
• dr inż. Tadeusz Miruszewski link otwiera się w nowej karcie ,
• dr hab. inż. Beata Bochentyn link otwiera się w nowej karcie ,
• dr hab. inż. Marcin Stanisław Łapiński link otwiera się w nowej karcie ,
• dr hab. inż. Jakub Karczewski link otwiera się w nowej karcie