A novel synthesis process was used to prepare TiO2 microspheres, TiO2 P-25, SrTiO3 and KTaO3 decorated by CdTe QDs and/or Pt NPs. The effect of semiconductor matrix, presence of CdTe QDs and/or Pt NPs on the semiconductor surface as well as deposition technique of Pt NPs (photodeposition or radiolysis) on the photocatalytic activity were investigated. The as-prepared samples were characterized by X-ray powder diffractometry (XRD), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM) with energy-dispersive X-ray (EDX) spectroscopy, scanning electron microscopy (SEM), photoluminescence spectrometry (PL), Fourier transform infrared (FT-IR) and Raman spectra, diffuse reflectance spectroscopy (DRS) and BET surface area analysis. The photocatalytic decomposition of toluene in gas phase, activated by light-emitting diodes (LEDs), with the CdTe/Pt nanoparticles-modified TiO2 microspheres, P25, SrTiO3 and KTaO3 semiconductors was investigated under UV–vis and visible irradiation.The results showed that the photoactivity depends on semiconductor matrix. The highest photoactivity under Vis light was observed for KTaO3/CdTe-Pt(R) sample (56% of toluene was decompose after 30 min of irradiation). The efficiency of the most active sample was 3 times higher than result for P25 and two times higher than for unmodified KTaO3.
Autorzy
- mgr inż. Martyna Marchelek,
- Dr. Ewelina Grabowska,
- prof. dr hab. inż. Tomasz Klimczuk link otwiera się w nowej karcie ,
- W. Lisowski,
- A. Zaleska-Medynska
Informacje dodatkowe
- DOI
- Cyfrowy identyfikator dokumentu elektronicznego link otwiera się w nowej karcie 10.1016/j.apsusc.2016.10.009
- Kategoria
- Publikacja w czasopiśmie
- Typ
- artykuł w czasopiśmie wyróżnionym w JCR
- Język
- angielski
- Rok wydania
- 2017