The main subject of this study are molecular structures and optical properties of boron-doped diamond films with [B]/[C] ppm ratio between 1000 and 10 000, fabricated in two molar ratios of CH 4 -H 2 mixture (1 % and 4 %). Boron-doped diamond (BDD) film on the fused silica was presented as a conductive coating for optical and electronic purposes. The scanning electron microscopy images showed homogenous and polycrystalline surface morphology. The Raman spectroscopy confirmed the growth of sp ³ diamond phase and sp ² carbon phase, both regular and amorphous, on the grain boundaries, as well as the efficiency of boron doping. The sp ³ /sp ² ratio was calculated using the Raman spectra deconvolution method. A high refractive index (in a range of 2.0 to 2.4 at λ = 550 nm) was achieved for BDD films deposited at 700 °C. The values of extinction coefficient were below 1.4 at λ = 550 nm, indicating low absorption of the film

Autorzy

• dr inż. Bartłomiej Dec link otwiera się w nowej karcie ,
• dr inż. Mateusz Ficek link otwiera się w nowej karcie ,
• dr inż. Michał Rycewicz link otwiera się w nowej karcie ,
• Łukasz Macewicz link otwiera się w nowej karcie ,
• dr hab. inż. Marcin Gnyba link otwiera się w nowej karcie ,
• Mirosław Sawczak,
• dr hab. inż. Michał Sobaszek link otwiera się w nowej karcie ,
• dr hab. inż. Robert Bogdanowicz link otwiera się w nowej karcie