Repozytorium publikacji - Politechnika Gdańska

Lanthanum niobate substituted with arsenic was synthesized by three methods: solid state reaction from binary oxides and two different methods combining co-precipitation and solidstate reaction. In the first of the combined methods LaNb1- xAsxO4 was synthesized from LaAsO4, obtained from coprecipitation method, and lanthanum and niobium oxides. In the second LaNbO4 was first synthesized from binary oxides and then mixed with LaAsO4 and fired in the second step to obtain the final material. Single phase materials could not be synthesized via solid-state synthesis, whilst it was possible with both of the combined methods. Structural parameters of the materials obtained with both methods were similar what shows that they do not relate to the synthesis method. Ceramics obtained with both combined methods were dense, however, the density of the ceramics formed from LaAsO4 and LaNbO4 was higher.

Autorzy

• dr inż. Sebastian Wachowski link otwiera się w nowej karcie ,
• dr inż. Bartosz Kamecki link otwiera się w nowej karcie ,
• dr inż. Piotr Winiarz link otwiera się w nowej karcie ,
• dr inż. Kacper Dzierzgowski link otwiera się w nowej karcie ,
• mgr inż. Michał Jurkowski link otwiera się w nowej karcie ,
• Jaroslav Dzisevič link otwiera się w nowej karcie ,
• dr hab. inż. Aleksandra Mielewczyk-Gryń link otwiera się w nowej karcie ,
• prof. dr hab. inż. Maria Gazda link otwiera się w nowej karcie