Composite materials consisting of acceptor doped lanthanum orthoniobate electrolyte phase (La0.98Ca0.02NbO4) and Li2O:NiO:ZnO semiconducting phase were synthesized. The precursor powder of La0.98Ca0.02NbO4 was prepared in nanocrystalline (mechanosynthesis) and microcrystalline (solid-state synthesis) form. The composite can be applied in a single-layer fuel cell, because of the presence of two phases acting as an anode and a cathode simultaneously. X-ray diffraction data show that the materials consist of two expected phases. Scanning Electron Microscope images, with Energy Dispersive X-Ray analysis show that La0.98Ca0.02NbO4 as well as Li2O:NiO:ZnO are mixed together in the volume of the material. Open circuit voltage both for nano- and microcrystalline composite do not exceed 0.8 V. The single-layer fuel cell is degrading upon time and the voltage drop is observed. The processes of ZnO reduction and Zn diffusion and evaporation as responsible for cell degradation are discussed.

Autorzy

• dr inż. Piotr Winiarz link otwiera się w nowej karcie ,
• dr inż. Tadeusz Miruszewski link otwiera się w nowej karcie ,
• dr inż. Sebastian Wachowski link otwiera się w nowej karcie ,
• dr inż. Kacper Dzierzgowski link otwiera się w nowej karcie ,
• dr inż. Iga Szpunar link otwiera się w nowej karcie ,
• mgr inż. Krzysztof Zagórski link otwiera się w nowej karcie ,
• dr hab. inż. Aleksandra Mielewczyk-Gryń link otwiera się w nowej karcie ,
• prof. dr hab. inż. Maria Gazda link otwiera się w nowej karcie