We report a systematic microstructural and electrical characterization of iron doped Mn–Co spinel coatings processed by electrophoretic co-deposition of Mn1.5Co1.5O4 and Fe2O3 powders on Crofer 22 APU and AISI 441 steel substrates. Iron addition to Mn–Co spinel coating leads to a reduction of the area specific resistance on both substrates, after 3200 h at 750 °C. The Fe doped Mn–Co coating both leads to a thinner oxide scale and reduces the sub scale oxidation for the Crofer 22 APU substrate. Fe doped Mn–Co on AISI 441 shows both a thicker oxide scale and low area specific resistance values, likely due to a doping effect of the oxide scale by minor alloying elements. The different mechanisms by which iron doping of Mn–Co spinels can influence elemental interdiffusion at the steel-oxide scale-coating interfaces and relative contributions to the overall area specific resistance are evaluated by means of advanced electron microscopy. The promising results are further confirmed in a cell test, where the Fe doped MnCo coated interconnect does not induce any degradation of the oxygen electrode, proving its efficiency.
Autorzy
- Elisa Zanchi,
- dr hab. inż. Sebastian Molin link otwiera się w nowej karcie ,
- A Sabato,
- B Talic,
- dr inż. Grzegorz Cempura,
- A Boccaccini,
- F Smeacetto
Informacje dodatkowe
- DOI
- Cyfrowy identyfikator dokumentu elektronicznego link otwiera się w nowej karcie 10.1016/j.jpowsour.2020.227910
- Kategoria
- Publikacja w czasopiśmie
- Typ
- artykuły w czasopismach
- Język
- angielski
- Rok wydania
- 2020