Repozytorium publikacji - Politechnika Gdańska

This work evaluates the effects of the sintering temperature (800 °C, 900 °C, 1000 °C) of SrTi1-xFexO3-δ (x = 0.35, 0.5, 0.7) porous electrodes on their electrochemical performance as potential oxygen electrode materials of solid oxide cells. The materials were prepared by a solid-state reaction method and revealed the expected cubic perovskite structure. After milling, the powders were characterised by a sub-micrometre particle size with high sinter-activity. It was shown that the lowest area specific resistance was achieved after sintering SrTi0.65Fe0.35O3 electrodes at 1000 °C, and SrTi0.5Fe0.5O3 and SrTi0.30Fe0.70O3 electrodes at 800 °C, which can be considered to be a relatively low temperature. In general, EIS measurements showed that increasing the Fe content results in lowered electrode polarisation and a decrease of the series resistance. Even though the studied materials have much lower total conductivities than state-of-the-art electrode materials (e.g. (La,Sr)(Co,Fe)O3), the polarisation resistances obtained in this work can be considered low.

Autorzy

• dr inż. Aleksander Mroziński link otwiera się w nowej karcie ,
• dr hab. inż. Sebastian Molin link otwiera się w nowej karcie ,
• prof. dr hab. inż. Piotr Jasiński link otwiera się w nowej karcie