Tin oxide is one of the most promising electrode materials as a negative electrode for lithium-ion batteries due to its higher theoretical specific capacity than graphite. However, it suffers lack of stability due to volume changes and low electrical conductivity while cycling. To overcome these issues, a new composite consisting of SnO2 and carbonaceous matrix was fabricated. Naturally abundant and renewable chitosan was chosen as a carbon source. The electrode material exhibiting 467 mAh g−1 at the current density of 18 mA g−1 and a capacity fade of only 2% after 70 cycles is a potential candidate for graphite replacement. Such good electrochemical performance is due to strong interaction between amine groups from chitosan and surface hydroxyl groups of SnO2 at the preparation stage. However, the charge storage is mainly contributed by a diffusion-controlled process showing that the best results might be obtained for low current rates

Autorzy

• dr hab. inż. Andrzej Nowak link otwiera się w nowej karcie ,
• prof. dr hab. inż. Maria Gazda link otwiera się w nowej karcie ,
• dr hab. inż. Marcin Łapiński link otwiera się w nowej karcie ,
• mgr inż. Zuzanna Zarach link otwiera się w nowej karcie ,
• dr inż. Konrad Trzciński link otwiera się w nowej karcie ,
• dr inż. Mariusz Szkoda link otwiera się w nowej karcie ,
• dr inż. Szymon Mania link otwiera się w nowej karcie ,
• Jinjin Li,
• dr hab. inż. Robert Tylingo link otwiera się w nowej karcie