Herein, highly crystalline ZrxNy and ZrxNyOz coatings are achieved by the deposition via high‐power impulse magnetron sputtering. Various N2 and N2/O2 gas mixtures with argon are investigated. The chemical composition and, as a result, mechanical properties of the deposited layer can be tailored along with morphological and crystallographic structural changes. The corrosion resistance behavior is studied by potentiodynamic measurements and electrochemical impedance spectroscopy in a sample of synthetic wastewater designed to imitate real‐life domestic wastewater. The corrosion current density of the ZrxNyOz coating is in the range of 33–70 μA cm−2, whereas for the zirconium nitride layers, values below 1.0 μA cm−2 are achieved. The highest corrosion resistance of 64 nm year−1 is observed for the ZrxNy coating deposited with 1.00% N2 content in the gas mixture with a corrosion potential of −0.41 V Ag/AgCl.

Autorzy

• dr inż. Anna Dettlaff link otwiera się w nowej karcie ,
• Mateusz Brodowski link otwiera się w nowej karcie ,
• Marcin Kowalski link otwiera się w nowej karcie ,
• Vitezslav Stranak,
• Vadym Prysiazhnyi,
• prof. dr hab. Ewa Klugmann-Radziemska link otwiera się w nowej karcie ,
• dr hab. inż. Jacek Ryl link otwiera się w nowej karcie ,
• dr hab. inż. Robert Bogdanowicz link otwiera się w nowej karcie