Polyurethane (PU) is one of the principal polymers in the global plastic market thanks to its versatility and continuous improvement. In this work, PU elastomeric materials having thermoregulating properties through the incorporation of microcapsules (mSD-(LDPE·EVA-RT27)) from low-density polyethylene and vinyl acetate containing paraffin®RT27 as PCM were produced. Elastomers were synthesized while varying the molar ratio [NCO]/[OH] between 1.05 and 1.1 and the microcapsule (MC) content from 0.0 to 20.0 wt.%. The successful synthesis of the PUs was confirmed by IR analyses. All the synthesized elastomers presented a structure formed by a net of spherical microparticles and with a minimum particle size for those with 10 wt.% MC. The density and tensile strength decreased with the MC content, probably due to worse distribution into the matrix. Elastomer E-1.05 exhibited better structural and stability properties for MC contents up to 15 wt.%, whereas E-1.1, containing 20 wt.% MC, revealed mechanical and thermal synergy effects, demonstrating good structural stability and the largest latent heat. Hence, elastomers having a large latent heat (8.7 J/g) can be produced by using a molar ratio [NCO]/[OH] of 1.1 and containing 20 wt.% mSD-(LDPE·EVA-RT27).

Autorzy

• prof. dr hab. inż. Janusz Datta link otwiera się w nowej karcie ,
• Patrycja Trzebiatowska,,
• Ana M. Borreguero,
• Irene Izarra,
• Ignacio Garrido,
• Angel Serrano,
• Professor Juan F. Rodríguez,
• PhD Manuel Carmona