Oxides in which total electrical conductivity is determined by the partial conductivities of three types of charge carriers i.e. holes/ electrons, oxygen ions, and protons are key components of well-functioning proton ceramic fuel cells. Apart from electrochemical properties also easily modified microstructure is an important feature of the electrodes. In the paper, a group of SrTi1−xFexO3−δ (STF, x = 0.2–0.8) perovskites prepared by solid-state synthesis was studied. The microstructure of ceramics was studied using SEM, and the results showed a significant influence of Fe amount on the grain size and material’s porosity. The electrical transport results show a different conductivity in a dry and humidified atmosphere. The hydration kinetics related to the water incorporation are presented with the transition from single-fold to two-fold behaviour, related to the proton-electron hole interaction observed in measurements. The obtained results strictly show a triple-conductivity of SrTi0.8Fe0.2O3−δ system at a lower temperature range, where the protonic defects are thermodynamically stable.

Autorzy

• dr inż. Tadeusz Miruszewski link otwiera się w nowej karcie ,
• dr inż. Wojciech Skubida link otwiera się w nowej karcie ,
• dr inż. Piotr Winiarz link otwiera się w nowej karcie ,
• dr inż. Kacper Dzierzgowski link otwiera się w nowej karcie ,
• dr hab. inż. Aleksandra Mielewczyk-Gryń link otwiera się w nowej karcie ,
• dr inż. Sebastian Wachowski link otwiera się w nowej karcie ,
• prof. dr hab. inż. Maria Gazda link otwiera się w nowej karcie