Here we demonstrate the application of hydroxyl-functionalized propylene-based copolymers, poly(propylene-co-1-hexene-co-10-undecen-1-ol) (FPP) and poly(styrene-co-maleic anhydride) (SMA) graft copolymers derived thereof, poly(propylene-co-1- hexene-graft-styrene-co-maleic anhydride) (FPP-g-SMA) as bitumen modifiers. The FPP samples were synthesized via solution copolymerization, while FPP-g-SMA products were obtained via transesterification of FPP with SMA either in solution or by a melt-grafting process. FPP-g-SMA modifiers prepared in solution, having a SMA content of around 30 wt.%, performed very well as compatibilizer for bitumen, generating a polymer-modified compositions with a uniform morphology and improved nanomechanical properties, storage stability, rheological properties and high- temperature performance as compared to neat bitumen samples.
Autorzy
- mgr inż. Mateusz Malus link otwiera się w nowej karcie ,
- dr Joanna Bojda link otwiera się w nowej karcie ,
- dr inż. Maciej Sienkiewicz link otwiera się w nowej karcie ,
- Miloud Bouyahyi,
- Lanti Yang,
- profesor Javier Francisco Navarro,
- Maria Soliman,
- Rob Duchateau,
- dr hab. inż. Lidia Jasińska-Walc link otwiera się w nowej karcie
Informacje dodatkowe
- DOI
- Cyfrowy identyfikator dokumentu elektronicznego link otwiera się w nowej karcie 10.1016/j.conbuildmat.2023.131630
- Kategoria
- Publikacja w czasopiśmie
- Typ
- artykuły w czasopismach
- Język
- angielski
- Rok wydania
- 2023