We report a successful synthesis of a high-purity intermetallic germanide Y2Pd1.25Ge2.75, crystallizing in the disordered variant of the AlB2-type structure. A single-phase sample was obtained via arc-melting by deliberately tuning the composition out of the ideal 2:1:3 ratio. Specific heat, electrical resistivity and magnetization measurements show that the compound is a weakly-coupled (λ e-p = 0.58) type-II superconductor with a superconducting transition at Tc = 2.72 K. Additional magnetization measurements conducted under pressure up to 0.55 GPa show suppression of Tc, at a rate of − 0.17 K/GPa. Electronic structure calculations reveal the deep similarity between Y2Pd1.25Ge2.75 and other AlB2-type germanide superconductors, especially the ordered YGa2 phase.

Autorzy

• Hanna Świątek link otwiera się w nowej karcie ,
• Szymon Królak link otwiera się w nowej karcie ,
• dr inż. Leszek Litzbarski link otwiera się w nowej karcie ,
• dr Ihor Oshchapovskyy link otwiera się w nowej karcie ,
• dr inż. Michał Winiarski link otwiera się w nowej karcie ,
• prof. dr hab. inż. Tomasz Klimczuk link otwiera się w nowej karcie