A hybrid system combining robocasting and NIR laser postprocessing has been designed to fabricate layers of mixed proton-electron conducting Ba0.5La0.5Co1-xFexO3-δ ceramic. The proposed manufacturing technique allows for the control of the geometry and microstructure and shortens the fabrication time to a range of a few minutes. Using 5 W laser power and a scanning speed of 500 mm⋅s− 1, sintering of a round-shaped layer with an 8 mm radius was performed in less than 2 s. The single phase of the final product was confirmed by X-ray diffraction. Various ceramic-to-polymer weight ratios were tested, showing that various porosities of microstructures of ~30 - 35 % and ~19 % can be obtained with 2:1 and 4:1 loading respectively.

Autorzy

• Joanna Pośpiech link otwiera się w nowej karcie ,
• Małgorzata Nadolska-Dawidowska,
• dr inż. Mateusz Cieślik link otwiera się w nowej karcie ,
• Tomasz Sobczyk link otwiera się w nowej karcie ,
• dr inż. Marek Chmielewski link otwiera się w nowej karcie ,
• dr hab. inż. Aleksandra Mielewczyk-Gryń link otwiera się w nowej karcie ,
• Dr Ragnar Strandbakke,
• José M Serra,
• dr inż. Sebastian Wachowski link otwiera się w nowej karcie