In this study, Co-bearing Metal-Organic Frameworks (MOFs) are grown via a facile solvothermal process on the surface of two kinds of conductive substrates – titanium dioxide nanotubes (TiO2NT) and fluorine-doped tin oxide (FTO) glass and tested as electrodes in the electrochemical hydrogen evolution reaction (HER). The materials derived from three organic linkers - terephthalic acid (Co-BDC), 2-aminoterephthalic acid (Co-BDCNH2), and trimesic acid (Co-BTC) are characterized by FTIR, Raman, XRD, SEM-EDS, BET, and XPS. Among the layers on FTO without post-synthesis treatment, Co-BTC shows the highest activity (overpotential of HER 1.72 V vs. Ag/AgCl/KCl). The effects of substrate change on TiO2NT and annealing of Co-BTC layers in air and argon on their electrocatalytic properties are also studied. Using TiO2 nanotubes as a substrate and annealing the material in air results in a reduction of the hydrogen evolution overpotential to 1.44 V vs. Ag/AgCl/KCl and a significant reduction in the exchange current density.

Autorzy

• dr inż. Natalia Łukasik link otwiera się w nowej karcie ,
• Daria Roda link otwiera się w nowej karcie ,
• Maria Alaide de Oliveira,
• Bráulio Silva Barros,
• dr inż. Joanna Kulesza,
• dr hab. inż. Marcin Łapiński link otwiera się w nowej karcie ,
• Hanna Świątek link otwiera się w nowej karcie ,
• Anna Ilnicka,
• prof. dr hab. inż. Tomasz Klimczuk link otwiera się w nowej karcie ,
• dr inż. Mariusz Szkoda link otwiera się w nowej karcie