This study investigates the influence of polymer interlayers on the mechanical properties and fracture behavior of friction stir welded EN AW-2024-T3 aluminum alloy joints. Aqualock AL 6002 (Adhesive_1) and 3M Adhesion Promoter 86A (Adhesive_2) were selected as polymeric sealants for EN AW-2024-T3 aluminum alloy interfaces. Force analysis revealed that the choice of polymer interlayer significantly affects the axial force during welding, with Adhesive_1 joints showing a significant reduction in force compared to other variants. The axial force during FSW in Adhesive_1 was 18% less than in Adhesive_2. Cross-sectional analysis revealed distinct features in joint morphology and defects, with Adhesive_1 joints exhibiting favorable thermal stability and minimal defects compared to Adhesive_2 joints. Tensile strength analysis showed a significant increase in load capacity for the Adhesive_1 (9470N) joint, while the Adhesive_2 (5030N) joint exhibited reduced strength due to inadequate heat flow. The Adhesive_1 joint showed a 93% increase in tensile strength compared to Adhesive_2. The mixing of Adhesive_2 with the joint area produced hard complex particles that reduced the strength of the final joint. Fracture analysis revealed complex fracture mechanisms, with Adhesive_1 joints exhibiting ductile fracture zones and Adhesive_2 joints exhibiting quasi-cleavable intergranular cracking. Microhardness distribution analysis showed variation between the joint variants, with Adhesive_2 joints showing higher microhardness in the weld nugget.

Autorzy

• Andrzej Kubit,
• Hamed Aghajani Derazkola,
• Piotr Myśliwiec,
• Paulina Szawara,
• Ján Slota,
• dr hab. inż. Wojciech Macek link otwiera się w nowej karcie