The eect of type (AgInS2, SnS, CuS2, Bi2S3) and amount (5, 10, 15 wt%) of quantum dots (QDs) on the surface properties and photocatalytic activity of QDs-sensitized TiO2 composite, was investigated. AgInS2, SnS, CuS2, Bi2S3 QDs were obtained by hot-injection, sonochemical, microwave, and hot-injection method, respectively. To characterize of as-prepared samples high-resolution transmission electron microscopy (HRTEM), scanning electron microscopy (SEM), X-ray diraction (XRD), UV-Vis spectroscopy and photoluminescence (PL) emission spectroscopy were applied. The size of AgInS2, SnS, CuS2, Bi2S3 QDs were 12; 2–6; 2–3, and 1–2 nm, respectively. The QDs and QDs-sensitized TiO2 composites obtained have been tested in toluene degradation under LEDs light irradiation (max = 415 nm and max = 375 nm). For pristine QDs the eciency of toluene degradation increased in the order of AgInS2 < Bi2S3 < CuS < SnS under 375 nm and AgInS2 < CuS < Bi2S3 < SnS under 415 nm. In the presence of TiO2/SnS QDs_15% composite, 91% of toluene was degraded after 1 h of irradiation, and this eciency was about 12 higher than that for pristine QDs under 375 nm. Generally, building the TiO2/AgInS2 and TiO2/SnS exhibited higher photoactivity under 375 nm than the pristine TiO2 and QDs which suggests a synergistic eect between QDs and TiO2 matrix.

Autorzy

• Anna Malankowska,
• Daria Kulesza,
• Jakub Sowik,
• Onur Cavdar,
• prof. dr hab. inż. Tomasz Klimczuk link otwiera się w nowej karcie ,
• doktor Grzegorz Trykowski,
• Prof. dr hab. inż. Adriana Zaleska-Medynska